ETD

• Cable sheathing
• Flame-Retardant
• Hydrothermal treatment
• Magnesium Hydroxide
• Polymeric compounds

In this work, hydrothermal treatments were carried out on magnesium hydroxide obtained from ground brucite. The aim was to enhance the value of this type of magnesium hydroxide, which, due to the grinding process used for its production, shows limited performance when used as a flame-retardant additive for cable sheathing. Specifically, it is characterized by a highly variable particle size distribution, morphological irregularity, and high moisture uptake. Different treatment times and temperatures were investigated in order to evaluate the effect of the operating conditions on the properties of the filler. Subsequently, a highly filled magnesium hydroxide composite material was prepared to assess whether the improvements observed in the powder also resulted in enhanced mechanical and rheological properties of the final product.

All'interno di questo lavoro sono stati applicati dei trattamenti idrotermali in autoclave sull'idrossido di magnesio ottenuto da brucite macinata. L'obiettivo è quello di valorizzare questa tipologia di idrossido di magnesio, che a causa del processo di macinazione con cui viene prodotto, presenta scarse proprietà quando lo si utilizza come additivo antifiamma per guaine di cavi, nello specifico: granulometria molto variabile, irregolarità morfologica, alto assorbimento di umidità. Sono stati indagati diversi tempi e temperature per valutare l'effetto delle condizioni operative sulle proprietà del filler. Successivamente, è stato realizzato un materiale composito ad alto caricamento di idrossido di magnesio indicativo di una guaina di cavo per valutare se i miglioramenti visualizzati sulla polvere portino anche miglioramenti sulle proprietà meccaniche e reologiche del prodotto.